C95500 Nickel Aluminum Bronze
C95500 Nickel Aluminum Bronze C95500 Nickel Aluminum Bronze C95500 Nickel Aluminum Bronze
C95500 Nickel Aluminum Bronze , Alloy Steel , Tool Steel , Electroplating , Electroplating Copper , Copper Alloys , Beryllium Copper , Stainless Steel , Plating , Alloys , Aluminum , Bronze Aluminum , Bronze Alloys , Sheet Aluminum , Aluminum Tube , Aluminum Tubing , Bronze Casting , Aluminum Alloys C95500 Nickel Aluminum Bronze , Alloy Steel , Tool Steel , Electroplating , Electroplating Copper , Copper Alloys , Beryllium Copper , Stainless Steel , Plating , Alloys , Aluminum , Bronze Aluminum , Bronze Alloys , Sheet Aluminum , Aluminum Tube , Aluminum Tubing , Bronze Casting , Aluminum Alloys
 
Brass Electrical Components
Brass Fasteners
Brass Inserts
Brass Hose Fittings
Brass Machined Parts Components
Brass Nuts
Brass Pipe Fittings
Brass Pressed Parts Components
Brass Sanitary Plumbing Fittings
Brass Screws
Brass Terminals
Brass Turned Parts
Brass Washers
Bronze Fittings Castings Parts
Cnc Machined Parts Components
Copper Parts Components
Copper Terminals Lugs
Stainless Steel Hose Fittings
Zinc Casting Parts
 
 

C95500 Nickel Aluminum Bronze :

 

Copper Alloy No. C95500

Aluminum Bronze 9D, CDA 955 Nickel Aluminum Bronze , Grade D

ASTM B 505 , ASTM B 271

Chemical Composition % by weight
 
Element
Nominal
Minimum
Maximum
Aluminum
11
10
11.5
Copper
81
78
-
Iron
4
3
5
Manganese
-
-
3.5
Nickel
4
3
5.5
 

Applications

Valve guides and seats in aircraft engines, corrosion resistant parts, bearings, bushings, gears, worm gears, pickling hooks and baskets, agitators.

Mechanical Properties (as cast)

M07 - As Continuous Cast
 
Hardness* Brinell Hardness (3000 kg load) 190
Tensile Strength** KSI 95 min
Yield Strength ** KSI (0.5% Ext. under load) 42 min
Elongation** % in 2 inch 10
 

**Test values are nominal approximations and depend on specimen size and orientation.
 

Physical Properties

Thermal Conductivity BTU/ (sq ft-ft-hr-F) 24.2
Specific Heat BTU/lb/ºF @ 68F .10
Thermal Expansion Per °F from 68 F to 572 F .000009
Density lb/cu in @ 68 F .272
Electrical Conductivity* (Annealed) % IACS @ 68 F 8.5
Modulus of Elasticity KSI 16,000
 

*Volume basis
 

Fabrication Practices

Stress relieving temperature 600 F or 316 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment Yes
Solution heat treating temperature 1585-1635 F or 860-890 C
Time at temperature 1 hour per inch of section thickness
Quenching medium Water or oil quench
Annealing temperature 1150-1225 F or 620-660 C
Time at temperature 1 hour per inch of section thickness
Machinability rating (Free Cutting Brass=100) 50
Suitability for being joined by: Soldering/Good
Brazing/Fair
Oxyacetylene Welding/Not Recommended
Carbon Arc Welding/Poor
Gas Shielded Arc Welding/Good
Coated Metal Arc Welding/Good
Related Words : C95500 Nickel Aluminum Bronze , Alloy Steel , Tool Steel , Electroplating , Electroplating Copper , Copper Alloys , Beryllium Copper , Stainless Steel , Plating , Alloys , Aluminum , Bronze Aluminum , Bronze Alloys , Sheet Aluminum , Aluminum Tube , Aluminum Tubing , Bronze Casting , Aluminum Alloys , Aluminum Nickel Bronze , National Bronze , Aluminum Plate , Aluminum Welding , Phosphor Bronze , Bronze Copper , Bronze Brass , Bronze Steel , Bronze Components , Aluminum Lead , Chemical Aluminum , Aluminum Wire
 
Please enquire here for C95500 Nickel Aluminum Bronze manufacturers exporters suppliers India China Jamnagar