C95400 9c Aluminum Bronze
C95400 9c Aluminum Bronze C95400 9c Aluminum Bronze C95400 9c Aluminum Bronze
Aluminium Bronze Foundry Castings Casting Parts Foundries , Castings , Foundries , Metal Casting , Investment Casting , Brass Castings , Investment Castings , Aluminum Casting , Metal Castings , Brass Casting , Aluminum Castings , Steel Castings , Metal Castings Foundries , Investment Casting Foundry , Aluminum Sand Casting , Aluminum , Alloy Casting , Aluminium Foundries , Aluminum Alloy Casting , Casting Mould , Alloy Castings , Casting Company , Bronze Foundries , Aluminum Die Casting , Casting Manufacturer , Aluminium Castings , Jewelry Castings , Casting Moulds , Alloy Die Casting , Aluminium Brass , Stainless Steel Castings , Aluminium Metals , Foundry Equipment , Aluminum Tubes
 
Brass Electrical Components
Brass Fasteners
Brass Inserts
Brass Hose Fittings
Brass Machined Parts Components
Brass Nuts
Brass Pipe Fittings
Brass Pressed Parts Components
Brass Sanitary Plumbing Fittings
Brass Screws
Brass Terminals
Brass Turned Parts
Brass Washers
Bronze Fittings Castings Parts
Cnc Machined Parts Components
Copper Parts Components
Copper Terminals Lugs
Stainless Steel Hose Fittings
Zinc Casting Parts
 
 

C95400 9c Aluminum Bronze :

 

Copper Alloy No. C95400

Aluminum Bronze 9C , CDA 954 , CuAl10Fe

ASTM B 505 , ASTM B 271

Chemical Composition % by weight
 
Element
Nominal
Minimum
Maximum
Aluminum
11
10
11.5
Copper
85
83
-
Iron
4
3
5
Manganese
-
-
.50
Nickel
-
-
2.5
 

Application for Castings

Bearings, gears, worm gears, bushings, wear plate, valve seats and guides, pickling hooks. 

Mechanical Properties (as cast)

M07 - As Continuous Cast
 
Hardness* Brinell Hardness (3000 kg load) 170
Tensile Strength** KSI 85 min
Yield Strength ** KSI (0.5% Ext. under load) 32 min
Elongation** % in 2 inch 10 min
 
**Test values are nominal approximations and depend on specimen size and orientation.
 

Physical Properties

Thermal Conductivity BTU/ (sq ft-ft-hr-F) 33.9
Specific Heat BTU/lb/ºF @ 68F .10
Thermal Expansion Per °F from 68 F to 572 F .000009
Density lb/cu in @ 68 F .269
Electrical Conductivity* (Annealed) % IACS @ 68 F 13
Modulus of Elasticity KSI 15,500
 

*Volume basis
 

Fabrication Practices

Stress relieving temperature 600 F or 316 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment Yes
Solution heat treating temperature 1600-1675 F or 870-910 C
Time at temperature 1 hour per inch of section thickness
Quenching medium Water
Annealing temperature 1150-1225 F or 620-660 C
Time at temperature 1 hour per inch of section thickness
Machinability rating (Free Cutting Brass=100) 60
Suitability for being joined by: Soldering/Good
Brazing/Good
Oxyacetylene Welding/Not Recommended
Carbon Arc Welding/Fair
Gas Shielded Arc Welding/Very Good
Coated Metal Arc Welding/Good
 
Related Words : C95400 9c Aluminum Bronze , Alloys , Copper Alloys , Beryllium Copper , Stainless Steel , Aluminum , Bronze Aluminum , Bronze Alloys , Sheet Aluminum , Aluminum Tube , Bronze Casting , Nickel Aluminum Bronze , Aluminum Tubing , Aluminum Plate , Bronze Castings , Aluminum Casting , Aluminum Welding , Phosphor Bronze , Bronze Copper , Nickel Bronze , Bronze Brass , Aluminum Bronze Plate , Aluminum Nickel , Bronze Wire , Bronze Components , Aluminum Composition , Bronze Bearing , Aluminum Rod , Aluminum Metals , Aluminum Wire ,
 
Please enquire here for C95400 9c Aluminum Bronze manufacturers exporters suppliers India China Jamnagar