C94800 Leaded Nickel Tin Bronze
C94800 Leaded Nickel Tin Bronze C94800 Leaded Nickel Tin Bronze C94800 Leaded Nickel Tin Bronze
C94800 Leaded Nickel Tin Bronze , Metal Plating , Titanium , Silver Plating , Copper Plating , Electroplating , Brass Plating , Plating , Copper Alloys , Aluminum , Bronze Alloys , Nickel Plating , Bronze , Nickel Metals , Bronze Castings , Bronze Wire , Aluminum Nickel , Metal Nickel , Nickel Silver C94800 Leaded Nickel Tin Bronze , Metal Plating , Titanium , Silver Plating , Copper Plating , Electroplating , Brass Plating , Plating , Copper Alloys , Aluminum , Bronze Alloys , Nickel Plating , Bronze , Nickel Metals , Bronze Castings , Bronze Wire , Aluminum Nickel , Metal Nickel , Nickel Silver
 
Brass Electrical Components
Brass Fasteners
Brass Inserts
Brass Hose Fittings
Brass Machined Parts Components
Brass Nuts
Brass Pipe Fittings
Brass Pressed Parts Components
Brass Sanitary Plumbing Fittings
Brass Screws
Brass Terminals
Brass Turned Parts
Brass Washers
Bronze Fittings Castings Parts
Cnc Machined Parts Components
Copper Parts Components
Copper Terminals Lugs
Stainless Steel Hose Fittings
Zinc Casting Parts
 
 

C94800 Leaded Nickel Tin Bronze :

 

Copper Alloy No. C94800

Leaded Nickel Tin Bronze CDA 948

ASTM B 505

Chemical Composition % by weight
 
Element
Nominal
Minimum
Maximum
Aluminum
-
-
.005
Antimony
-
-
.15
Copper
86.5
84
89
Iron
-
-
.25
Lead
.70
.30
1
Manganese
-
-
.20
Nickel
5.3
4.5
6
Phosphorus
-
-
.05
Silicon
-
-
.005
Sulfur
-
-
.05
Tin
5
4.5
6
Zinc
1.8
1
2.5
 

Applications

Structural castings, gear components, motion translation devices, machinery parts, bearings.

Mechanical Properties

M07 - As Continuous Cast
 
Hardness* Brinell Hardness (500 kg load) 80
Tensile Strength** KSI 40 min
Yield Strength ** KSI (0.5% Ext. under load) 20 min
Elongation** % in 2 inch 20 min
 
**Test values are nominal approximations and depend on specimen size and orientation.
 

Physical Properties

Thermal Conductivity BTU/ (sq ft-ft-hr-F) 22.3
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 572 F .000011
Density lb/cu in @ 68 F .320
Electrical Conductivity* (Annealed) % IACS @ 68 F 12
Modulus of Elasticity KSI 15,000
 
*Volume basis
 

Fabrication Practices

Stress relieving temperature 500 F or 260 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment Yes
Machinability rating (Free Cutting Brass=100) 50
Suitability for being joined by: Soldering/Excellent
Brazing/Good*
Oxyacetylene Welding/Not Recommended
Carbon Arc Welding/Not Recommended
Gas Shielded Arc Welding/Not Recommended
Coated Metal Arc Welding/Not Recommended
 
Related Words : C94800 Leaded Nickel Tin Bronze , Metal Plating , Titanium , Silver Plating , Copper Plating , Electroplating , Brass Plating , Plating , Copper Alloys , Aluminum , Bronze Alloys , Nickel Plating , Bronze , Nickel Metals , Bronze Castings , Bronze Wire , Aluminum Nickel , Metal Nickel , Nickel Silver , Bronze Casting , Aluminum Bronze , Copper Nickel , Phosphor Bronze , Bronze Steel , Aluminium Nickel , Bronze Silver , Zinc Nickel , Bronze Metal , Aluminum Tin , Bronze Copper
 