C94300 High Leaded Tin Bronze
C94300 High Leaded Tin Bronze C94300 High Leaded Tin Bronze C94300 High Leaded Tin Bronze
C94300 High Leaded Tin Bronze , Aluminum Casting , Alloys , Beryllium Copper , Copper Alloys , Aluminum , Leaded Tin Bronze , Bronze Alloys , Bronze , Bronze Castings , Bronze Wire , Aluminium Bronze , Nickel Bronze , Aluminum Bronze Bar , Bronze Casting , Aluminum Bronze , Nickel Aluminum Bronze , Phosphor Bronze , Bronze Steel , Bronze Rod , Bronze Silver C94300 High Leaded Tin Bronze , Aluminum Casting , Alloys , Beryllium Copper , Copper Alloys , Aluminum , Leaded Tin Bronze , Bronze Alloys , Bronze , Bronze Castings , Bronze Wire , Aluminium Bronze , Nickel Bronze , Aluminum Bronze Bar , Bronze Casting , Aluminum Bronze , Nickel Aluminum Bronze , Phosphor Bronze , Bronze Steel , Bronze Rod , Bronze Silver
 
Brass Electrical Components
Brass Fasteners
Brass Inserts
Brass Hose Fittings
Brass Machined Parts Components
Brass Nuts
Brass Pipe Fittings
Brass Pressed Parts Components
Brass Sanitary Plumbing Fittings
Brass Screws
Brass Terminals
Brass Turned Parts
Brass Washers
Bronze Fittings Castings Parts
Cnc Machined Parts Components
Copper Parts Components
Copper Terminals Lugs
Stainless Steel Hose Fittings
Zinc Casting Parts
 
 

C94300 High Leaded Tin Bronze :

 

Copper Alloy No. C94300

High Leaded Tin Bronze CDA 943

ASTM B 505 , ASTM B 271

Chemical Composition % by weight
 
Element
Nominal
Minimum
Maximum
Aluminum
-
-
.005
Antimony
-
-
.8
Copper
69.5
67
72
Iron
-
-
.15
Lead
25
23
27
Nickel
-
-
1
Phosphorus
-
-
.05
Silicon
-
-
.005
Sulfur
-
-
.08
Tin
5.3
4.5
6
Zinc
-
-
.8
 

Applications

High speed bearings for light loads

Mechanical Properties

M07 - As Continuous Cast
 
Hardness* Brinell Hardness (500 kg load) 48
Tensile Strength** KSI 21 min
Yield Strength ** KSI (0.5% Ext. under load) 15 min
Elongation** % in 2 inch 7 min
 

**Test values are nominal approximations and depend on specimen size and orientation.
 

Physical Properties

Thermal Conductivity BTU/ (sq ft-ft-hr-F) 36.2
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 392 F N/A
Density lb/cu in @ 68 F .336
Electrical Conductivity* (Annealed) % IACS @ 68 F 9
Modulus of Elasticity KSI 10,500
 
*Volume basis
 

Fabrication Practices

Stress relieving temperature 500 F or 260 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment No
Machinability rating (Free Cutting Brass=100) 80
Suitability for being joined by: Soldering/Good
Brazing/Poor*
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Not Recommended
Coated Metal Arc Welding/Not Recommended
 
Related Words : C94300 High Leaded Tin Bronze , Aluminum Casting , Alloys , Beryllium Copper , Copper Alloys , Aluminum , Leaded Tin Bronze , Bronze Alloys , Bronze , Bronze Castings , Bronze Wire , Aluminium Bronze , Nickel Bronze , Aluminum Bronze Bar , Bronze Casting , Aluminum Bronze , Nickel Aluminum Bronze , Phosphor Bronze , Bronze Steel , Bronze Rod , Bronze Silver , Aluminum Bronze Rod , Leaded Copper , Bronze Metal , Aluminum Tin , Copper Tin , Bronze Copper , Bronze Brass , Stainless Bronze , Aluminum Bronze Tubing , Bronze Components
 