C94100 High Leaded Tin Bronze
C94100 High Leaded Tin Bronze C94100 High Leaded Tin Bronze C94100 High Leaded Tin Bronze
C94100 High Leaded Tin Bronze , Aluminum Casting , Aluminum Castings , Beryllium Copper , Alloys , Beryllium Copper , Copper Alloys , Aluminum , Bronze Alloys , Bronze , Bronze Castings , Bronze Wire , Aluminium Bronze , Nickel Bronze , Aluminum Bronze Bar , Bronze Casting , Aluminum Bronze C94100 High Leaded Tin Bronze , Aluminum Casting , Aluminum Castings , Beryllium Copper , Alloys , Beryllium Copper , Copper Alloys , Aluminum , Bronze Alloys , Bronze , Bronze Castings , Bronze Wire , Aluminium Bronze , Nickel Bronze , Aluminum Bronze Bar , Bronze Casting , Aluminum Bronze
 
Brass Electrical Components
Brass Fasteners
Brass Inserts
Brass Hose Fittings
Brass Machined Parts Components
Brass Nuts
Brass Pipe Fittings
Brass Pressed Parts Components
Brass Sanitary Plumbing Fittings
Brass Screws
Brass Terminals
Brass Turned Parts
Brass Washers
Bronze Fittings Castings Parts
Cnc Machined Parts Components
Copper Parts Components
Copper Terminals Lugs
Stainless Steel Hose Fittings
Zinc Casting Parts
 
 

C94100 High Leaded Tin Bronze :

 

Copper Alloy No. C94100

High Leaded Tin Bronze SAE 94 , CDA 941

ASTM B 505

Chemical Composition % by weight
 
Element
Nominal
Minimum
Maximum
Aluminum
-
-
.005
Copper
75.5
72
79
Iron
-
-
.25
Lead
20
18
22
Nickel
-
-
1
Phosphorus
-
-
.05
Silicon
-
-
.005
Sulfur
-
-
.08
Tin
5.5
4.5
6.5
Zinc
-
-
1
 

Applications

High speed bearings for light loads.

Mechanical Properties

M07 - As Continuous Cast
 
Hardness* Brinell Hardness (500 kg load) 52
Tensile Strength** KSI 25
Yield Strength ** KSI (0.5% Ext. under load) 17
Elongation** % in 2 inch 16
 

**Test values are nominal approximations and depend on specimen size and orientation.
 

Physical Properties

Thermal Conductivity BTU/ (sq ft-ft-hr-F) 36.2
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 392 F N/A
Density lb/cu in @ 68 F .336
Electrical Conductivity* (Annealed) % IACS @ 68 F 9
Modulus of Elasticity KSI 10,500
 

*Volume basis
 

Fabrication Practices

Stress relieving temperature 500 F or 260 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment No
Machinability rating (Free Cutting Brass=100) 75
Suitability for being joined by: Soldering/Good
Brazing/Poor*
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Not Recommended
Coated Metal Arc Welding/Not Recommended
 
Related Words : C94100 High Leaded Tin Bronze , Aluminum Casting , Aluminum Castings , Beryllium Copper , Alloys , Beryllium Copper , Copper Alloys , Aluminum , Bronze Alloys , Bronze , Bronze Castings , Bronze Wire , Aluminium Bronze , Nickel Bronze , Aluminum Bronze Bar , Bronze Casting , Aluminum Bronze , Nickel Aluminum Bronze , Phosphor Bronze , Bronze Steel , Bronze Rod , Silicon Bronze Bar , Aluminum Bronze Rod , Leaded Copper , Bronze Metal , Aluminum Tin , Bronze Copper , Bronze Brass , Bronze Bar , Bronze Components
 