C93700 High Leaded Tin Bronze , Aluminum Casting , Aluminum Castings , Alloys , Beryllium Copper , Copper Alloys , Aluminum , Bronze Alloys , Bronze , Bronze Castings , Bronze Wire , Aluminium Bronze , Nickel Bronze , Aluminum Bronze Bar , Bronze Casting , Aluminum Bronze , Nickel Aluminum Bronze , Phosphor Bronze , Bronze Steel , Bronze Rod , Bronze Silver C93700 High Leaded Tin Bronze , Aluminum Casting , Aluminum Castings , Alloys , Beryllium Copper , Copper Alloys , Aluminum , Bronze Alloys , Bronze , Bronze Castings , Bronze Wire , Aluminium Bronze , Nickel Bronze , Aluminum Bronze Bar , Bronze Casting , Aluminum Bronze , Nickel Aluminum Bronze , Phosphor Bronze , Bronze Steel , Bronze Rod , Bronze Silver
 
Brass Electrical Components
Brass Fasteners
Brass Inserts
Brass Hose Fittings
Brass Machined Parts Components
Brass Nuts
Brass Pipe Fittings
Brass Pressed Parts Components
Brass Sanitary Plumbing Fittings
Brass Screws
Brass Terminals
Brass Turned Parts
Brass Washers
Bronze Fittings Castings Parts
Cnc Machined Parts Components
Copper Parts Components
Copper Terminals Lugs
Stainless Steel Hose Fittings
Zinc Casting Parts
 
 

C93700 High Leaded Tin Bronze :

 

Copper Alloy No. C93700

High Leaded Tin Bronze SAE 64 , CDA 937 , 80-10-10

ASTM B 505 , ASTM B 271

Chemical Composition % by weight
 
Element
Nominal
Minimum
Maximum
Aluminum
-
-
.005
Antimony
-
-
.55
Copper
80
78
82
Iron
-
-
.15
Lead
10
8
11
Nickel
-
-
1
Phosphorus
-
-
.15
Silicon
-
-
.005
Sulfur
-
-
.08
Tin
10
9
11
Zinc
-
-
.8
 

C93700 has excellent machining properties, medium strength and good corrosion resistance and will withstand mild acids as found in mine water.
 

Bearings manufactured from C93700 have excellent wear resistance under conditions of high speed, heavy pressure and vibration, have low friction and can be used where lubrication is less than adequate and there may be minor misalignment. C93700 bearings require a hardened shaft and maximum shaft surface speeds of 4 m/sec can be tolerated.
 
Applications

Bearings for high speed and heavy pressures, pumps, impellers, corrosion resistant applications, pressure tight castings. 

Mechanical Properties

M07 - As Continuous Cast
 
Hardness* Brinell Hardness (500 kg load) 60
Tensile Strength** KSI 35
Yield Strength ** KSI (0.5% Ext. under load) 20
Elongation** % in 2 inch 20
 

**Test values are nominal approximations and depend on specimen size and orientation.
 

Physical Properties

Thermal Conductivity BTU/ (sq ft-ft-hr-F) 27.1
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 392 F .0000103
Density lb/cu in @ 68 F .320
Electrical Conductivity* (Annealed) % IACS @ 68 F 10
Modulus of Elasticity KSI 11,000
 

*Volume basis
 

Fabrication Practices

Stress relieving temperature 500 F or 260 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment No
Machinability rating (Free Cutting Brass=100) 80
Suitability for being joined by: Soldering/Good
Brazing/Good*
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Not Recommended
Coated Metal Arc Welding/Not Recommended
 
Related Words : C93700 High Leaded Tin Bronze , Aluminum Casting , Aluminum Castings , Alloys , Beryllium Copper , Copper Alloys , Aluminum , Bronze Alloys , Bronze , Bronze Castings , Bronze Wire , Aluminium Bronze , Nickel Bronze , Aluminum Bronze Bar , Bronze Casting , Aluminum Bronze , Nickel Aluminum Bronze , Phosphor Bronze , Bronze Steel , Bronze Rod , Bronze Silver , Aluminum Bronze Rod , Leaded Copper , Aluminum Tin , Bronze Metal , Bronze Copper , Bronze Brass , Components Of Bronze , Aluminum Bronze Tubing , Bronze Components ,
 