C93400 High Leaded Tin Bronze
C93400 High Leaded Tin Bronze C93400 High Leaded Tin Bronze C93400 High Leaded Tin Bronze
C93400 High Leaded Tin Bronze , Aluminum Casting , Aluminum Castings , Brazing , Beryllium Copper , Alloys , Copper Alloys , Aluminum , Leaded Tin Bronze , Bronze Alloys ,Bronze , Bronze Wire , Bronze Castings , Aluminium Bronze , Nickel Bronze , Manganese Bronze , Aluminum Bronze Bar , Bronze Casting , Aluminum Bronze , Nickel Aluminum Bronze , Phosphor Bronze , Bronze Steel C93400 High Leaded Tin Bronze , Aluminum Casting , Aluminum Castings , Brazing , Beryllium Copper , Alloys , Copper Alloys , Aluminum , Leaded Tin Bronze , Bronze Alloys ,Bronze , Bronze Wire , Bronze Castings , Aluminium Bronze , Nickel Bronze , Manganese Bronze , Aluminum Bronze Bar , Bronze Casting , Aluminum Bronze , Nickel Aluminum Bronze , Phosphor Bronze , Bronze Steel
 
Brass Electrical Components
Brass Fasteners
Brass Inserts
Brass Hose Fittings
Brass Machined Parts Components
Brass Nuts
Brass Pipe Fittings
Brass Pressed Parts Components
Brass Sanitary Plumbing Fittings
Brass Screws
Brass Terminals
Brass Turned Parts
Brass Washers
Bronze Fittings Castings Parts
Cnc Machined Parts Components
Copper Parts Components
Copper Terminals Lugs
Stainless Steel Hose Fittings
Zinc Casting Parts
 
 

C93400 High Leaded Tin Bronze :

 

Copper Alloy No. C93400

High Leaded Tin Bronze CDA 934

ASTM B 505

Chemical Composition % by weight
 
Element
Nominal
Minimum
Maximum
Aluminum
-
-
.005
Antimony
-
-
.50
Copper
84
82
85
Iron
-
-
.15
Lead
8
7
9
Nickel
-
-
1
Phosphorus
-
-
.50
Silicon
-
-
.005
Sulfur
-
-
.08
Tin
8
7
9
Zinc
-
-
.8
 

Applications

Bearings and bushings 

Mechanical Properties

M07 - As Continuous Cast
 
Hardness* Brinell Hardness (500 kg load) 60
Tensile Strength** KSI 34 min
Yield Strength ** KSI (0.5% Ext. under load) 20 min
Elongation** % in 2 inch 8 min
 
**Test values are nominal approximations and depend on specimen size and orientation.
 

Physical Properties

Thermal Conductivity BTU/ (sq ft-ft-hr-F) 33.6
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 392 F .000010
Density lb/cu in @ 68 F .320
Electrical Conductivity* (Annealed) % IACS @ 68 F 12
Modulus of Elasticity KSI 11,000
 

*Volume basis
 

Fabrication Practices

Stress relieving temperature 500 F or 260 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment No
Machinability rating (Free Cutting Brass=100) 70
Suitability for being joined by: Soldering/Good
Brazing/Good*
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Not Recommended
Coated Metal Arc Welding/Not Recommended
 
Related Words : C93400 High Leaded Tin Bronze , Aluminum Casting , Aluminum Castings , Brazing , Beryllium Copper , Alloys , Copper Alloys , Aluminum , Leaded Tin Bronze , Bronze Alloys ,Bronze , Bronze Wire , Bronze Castings , Aluminium Bronze , Nickel Bronze , Manganese Bronze , Aluminum Bronze Bar , Bronze Casting , Aluminum Bronze , Nickel Aluminum Bronze , Phosphor Bronze , Bronze Steel , Bronze Rod , Bronze Silver , Aluminum Bronze Rod , Bronze Metal , Bronze Brass , Stainless Bronze , Aluminum Bronze Tubing , Bronze Components , Silicon Bronze Plate
 